Semiconductor device

ABSTRACT

A semiconductor device includes plural semiconductor fins and a gate structure over at least one of the semiconductor fins. The semiconductor fins have parallelogram top surfaces, and the parallelogram top surface has two acute interior angles and two obtuse interior angles. Two of the semiconductor fins are arranged along &lt; 110 &gt; crystallographic direction, and two of the semiconductor fins are arranged along &lt; 100 &gt; crystallographic direction.

PRIORITY CLAIM AND CROSS-REFERENCE

This application is a divisional application of U.S. patent application Ser. No. 15/988,496, filed May 24, 2018, now U.S. Pat. No. 10,672,889, issued Jun. 2, 2020, which claims priority of U.S. Provisional Application Ser. No. 62/593,171, filed Nov. 30, 2017, the entirety of which is incorporated by reference herein in their entireties.

BACKGROUND

Combining the different groups of semiconductor materials in semiconductor structures will provide a range of performance benefits for various semiconductor devices formed on the semiconductor structures. However, problems arise when layering various semiconductor materials, especially between group III/V and group IV materials. Semiconductors are crystalline materials that have lattice structures. The different semiconductor groups and semiconductors within the same group may have varying lattice constants. When epitaxially growing a semiconductor material with a second lattice constant on a semiconductor material with a first lattice constant, defects may occur. Some of the defects may be threading dislocations. High threading dislocation density, stemming from large lattice mismatch, may render the semiconductor device unusable. Threading dislocations may occur when growing a crystal structure on another crystal structure with a different lattice constant. They are defects within the crystal structure itself.

BRIEF DESCRIPTION OF THE DRAWINGS

Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIGS. 1(A)-1(C) are schematic diagrams showing the three types of crystalline orientation for silicon.

FIG. 2 is a flow chart illustrating a method of fabricating a semiconductor device in accordance with some embodiments of the instant disclosure.

FIGS. 3-12 depict schematic perspective views in various intermediate stages of forming a semiconductor fin.

FIG. 13 depicts a schematic view of a semiconductor wafer and a trench.

FIG. 14 depicts a cross-sectional schematic view along line I-I in FIG. 8.

FIG. 15 depicts a local top view of the semiconductor fins of FIG. 12.

FIGS. 16A-16C depict schematic simplified structure of a semiconductor device.

FIGS. 17A-17C depict schematic simplified structure of a semiconductor device.

DETAILED DESCRIPTION

The following disclosure provides many different embodiments, or examples, for implementing different features of the provided subject matter. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.

The fins may be patterned by any suitable method. For example, the fins may be patterned using one or more photolithography processes, including double-patterning or multi-patterning processes. Generally, double-patterning or multi-patterning processes combine photolithography and self-aligned processes, allowing patterns to be created that have, for example, pitches smaller than what is otherwise obtainable using a single, direct photolithography process. For example, in one embodiment, a sacrificial layer is formed over a substrate and patterned using a photolithography process. Spacers are formed alongside the patterned sacrificial layer using a self-aligned process. The sacrificial layer is then removed, and the remaining spacers may then be used to pattern the fins.

Silicon (Si) is recognized as presently being the most ubiquitous semiconductor substrate for the electronics industry. Most of silicon that is used to form silicon wafers is formed from single crystal silicon. The silicon wafers serve as the substrate on which complementary metal-oxide-semiconductor (CMOS) devices are formed. In crystalline silicon, the atoms which make up the solid are arranged in a periodic fashion. If the periodic arrangement exists throughout the entire solid, the substance is defined as being formed of a single crystal. If the solid is composed of a myriad of single crystal regions the solid is referred to as polycrystalline material. As readily understood by skilled artisans, periodic arrangement of atoms in a crystal is called the lattice. The crystal lattice also contains a volume which is representative of the entire lattice and is referred to as a unit cell that is regularly repeated throughout the crystal. For example, silicon has a diamond cubic lattice structure, which can be represented as two interpenetrating face-centered cubic lattices. Thus, the simplicity of analyzing and visualizing cubic lattices can be extended to characterization of silicon crystals. In the description herein, references to various planes in silicon crystals will be made, especially to the (100), (110), and (111) planes. These planes define the orientation of the plane of silicon atoms relative to the principle crystalline axes. The numbers {xyz} are referred to as Miller indices and are determined from the reciprocals of the points at which the crystal plane of silicon intersects the principle crystalline axes.

FIGS. 1(A) through 1(C) show three orientations of the crystal plane of silicon. In FIG. 1(A), the crystal plane of silicon intersects the x-axis at 1 and never intersects the y or z-axis. Therefore, the orientation of this type of crystalline silicon is (100). Similarly, FIG. 1(B) shows (110) crystalline silicon and FIG. 1(C) shows (111) silicon. The (100) orientation is the primary wafer orientation in commercial use. Notably, for any given plane in a cubic crystal there are five other equivalent planes. Thus, the six sides of the cube comprising the basic unit cell of the crystal are all considered (100) planes. The notation {xyz} refers to all six of the equivalent (xyz) planes. Throughout the description, reference will also be made to the crystal directions, especially the <100>, <110> and <111> directions. These are defined as the normal direction to the respective plane. Thus, the <100> direction is the direction normal to the (100) plane. The notation <xyz> refers to all six equivalent directions.

Referring to FIG. 2, a flow chart of a method 100 of fabricating a semiconductor device in accordance with some embodiments of the instant disclosure. The method 100 begins with operation 110 in which a semiconductor pillar is formed on a semiconductor substrate along an <xyz> crystallographic direction. The method 100 continues with operation 120 in which an isolation layer is deposited on the semiconductor substrate and around the semiconductor pillar. Subsequently, operation 130 is performed. The semiconductor pillar is removed to form a trench. The method 100 continues with operation 140 in which an epitaxial layer is grown in the trench. The method 100 continues with operation 150 in which a hard mask orientated along an <x′y′z′> crystallographic direction is formed over the epitaxial layer. The method 100 continues with operation 160 in which the epitaxial layer is patterned according to the hard mask to form a semiconductor fin. The discussion that follows illustrates embodiments of semiconductor devices that can be fabricated according to the method 100 of FIGS. 1(A)-(C). While method 100 is illustrated and described below as a series of acts or events, it will be appreciated that the illustrated ordering of such acts or events are not to be interpreted in a limiting sense. For example, some acts may occur in different orders and/or concurrently with other acts or events apart from those illustrated and/or described herein. In addition, not all illustrated acts may be required to implement one or more aspects or embodiments of the description herein. Further, one or more of the acts depicted herein may be carried out in one or more separate acts and/or phases.

Reference is made to FIG. 3. A semiconductor substrate 310 is provided that includes a first semiconductor material, such as, for example, a group IV element, e.g., germanium or silicon. The first semiconductor material may be crystalline. The semiconductor substrate 310 may be, for example, a bulk silicon wafer, a bulk germanium wafer, a semiconductor-on-insulator (SOI) substrate, or a strained semiconductor-on-insulator (SOI) substrate. In some embodiments, the substrate 310 includes (001) silicon. The substrate 310 may include a material having a first conductivity type, e.g., n- or p-type, such as n+Si.

Reference is made to FIG. 4. Semiconductor pillars 312 are formed on the semiconductor substrate 310. A photolithography and patterning process may be performed to form the semiconductor pillars 312. A mask (not shown) is disposed over the semiconductor substrate 310 and developed to define the semiconductor pillars 312 extending along a first crystallographic direction D1 of the first semiconductor material. The first crystallographic direction D1 has a notation <xyz>. In some embodiments, <xyz> can be <100>. Then a positive or negative etching process is performed. At least a portion of the semiconductor pillars 312 sidewall is generally vertical, i.e. disposed at about 80 to 120 degrees to the surface of the semiconductor substrate 310. In some embodiments, the sidewalls of the semiconductor pillars 312 are substantially perpendicular to the surface of the semiconductor substrate 310. In some embodiments, the semiconductor pillars 312 are elongated rectangular bars, spanning across the surface of the semiconductor substrate 310. The semiconductor pillars 312 are spaced apart by a predetermined pitch and substantially parallel to each other as shown in FIG. 4. The length of the semiconductor pillars 312 may vary on one semiconductor substrate 310 due to the shape of the wafer. The number of the semiconductor pillars 312 may vary depending on design choice.

Reference is made to FIG. 5. An isolation region 314 is formed. A dielectric material is blanket deposited over the semiconductor substrate 310 and covers up the semiconductor pillars 312. In some embodiments, the dielectric material includes un-doped oxide material, for example, SiO₂. The formation of isolation region 314 may be performed using high-density plasma chemical vapor deposition (HDPCVD). Other suitable methods, such as sub-atmospheric CVD (SACVD) and spin-on can also be used. A chemical mechanical polish (CMP) is then performed to remove excess dielectric material until the underlying semiconductor pillars 312 are exposed. The semiconductor pillars 312 may be seen as the active region surrounded by the isolation region 314 on the semiconductor substrate 310.

Reference is made to FIG. 6. The semiconductor pillars 312 are removed. The semiconductor pillars 312 are orientated along <100> crystallographic direction of the first semiconductor material. When the semiconductor pillars 312 of FIG. 4 are removed by, for example, dry etching, trenches 316 are formed in the isolation region 314. These trenches 316 retain the bar-like shapegoing along the <100> crystallographic direction over the semiconductor substrate 310. Sidewalls of the trenches 316 inherit the geometrical property of the semiconductor pillars 312. The trenches are used as a mold to grow an epitaxial layer in the subsequent process. In some embodiments, the trenches 316 are sufficiently deep so as to fulfil the geometrical conditions in aspect-ratio-trapping (ART). In some embodiments, the height of the isolation region 314 is equivalent to the height of the trenches 316. That is, the trenches 316 expose the semiconductor substrate 310. In some embodiments, the semiconductor pillars 312 are partially removed and portions thereof remain at the bottom of the trenches 316. In that case, the height of the isolation region 314 is larger than the height of the trenches 316. In some embodiments, the trenches 316 have a depth of about 120 nm.

Reference is made to FIG. 7. An epitaxial layer 318 is formed in the trenches 316. The isolation region 314, as described below in greater detail, is used as a dislocation-blocking mask. The epitaxial layer 318 that includes a second semiconductor material is deposited in the trenches 316. The epitaxial layer may be formed in the opening by selective epitaxial growth in any suitable epitaxial deposition system, including, but not limited to, atmospheric-pressure CVD (APCVD), low- (or reduced-) pressure CVD (LPCVD), ultra-high-vacuum CVD (UHVCVD), by molecular beam epitaxy (MBE), or by atomic layer deposition (ALD). In the CVD process, selective epitaxial growth typically includes introducing a source gas into the chamber. The source gas may include at least one precursor gas and a carrier gas, such as, for example hydrogen. The reactor chamber is heated, such as, for example, by RF-heating. The growth temperature in the chamber ranges from about 300° C. to about 900° C. depending on the composition of the regrowth layer. The growth system may utilize low-energy plasma to enhance the layer growth kinetics. If the epitaxial material excesses the trenches 316, a planarization process (such as a CMP process) can be performed to remove the excess epitaxial material.

In some embodiments, the first semiconductor material may include silicon or a silicon germanium alloy. The second semiconductor material may include a group III, a group IV, a group V, and/or combinations thereof, for example, selected from the group consisting of germanium, silicon germanium, gallium arsenide, aluminium antimonide, indium aluminium antimonide, indium antimonide, indium arsenide, indium phosphide, and gallium nitride. In some embodiments, the first semiconductor material is silicon and the second semiconductor material is silicon germanium. Since the material of the semiconductor substrate 310 is different from that of the epitaxial layer 318, the epitaxial process can be referred to as heteroepitaxy.

Reference is made to FIG. 13. When fabricating semiconductor heterostructures, substrate interface defects occurs in a variety of lattice-mismatched materials systems. Metal oxide semiconductor (MOS) transistors are typically fabricated on (100) silicon wafers with the gates oriented such that current flows parallel to the <110> directions. In FIG. 13, dotted lines represent the threading dislocations 390 that are generated during epitaxial growth along <111> family, including [111], [−111], [−1−11], and [−1−1−1] crystallographic directions. The term “threading dislocation” refers to dislocations originating from a substrate and propagating into the epitaxial layers above it, colloquially it refers to dislocations inclined to the plane of the substrate and propagating through the epitaxial layer at some non-normal angle to the growth axis. The term “threading dislocation” will be used in its colloquial sense hereinafter.

The semiconductor substrate 310 is schematically shown as a standard wafer with a notch at [110] orientation. The trenches 316 does not align with the [110] orientation but tilts approximately 45 degrees to the notch along the [100] orientation. The <100> crystallographic direction enables confinement of the <111> crystallographic direction family threading dislocations 390. Because of the configuration of the underlying semiconductor surface, orientation of the threading dislocations 390 in the heteroepitaxial region (i.e., in the trenches 316) is at approximately 54 degrees to the surface of the semiconductor substrate 310. The vertical sidewalls of the trenches 316 (i.e., isolation region 314) facilitate trapping of the threading dislocations 390, which develop into [111], [−111], [−1−11], and [−1−1−1] orientations, as shown in FIG. 13.

Reference is made to FIG. 8. A hard mask 320 is disposed on the isolation region 314. A photolithography and etching process may be performed to form the hard mask 320 into a plurality of separate strips that are arranged along a second crystallographic direction D2 of the first semiconductor material. The second crystallographic direction D2 has a notation <x′y′z′> different from the notation <xyz> mentioned above. In some embodiments, <x′y′z′> can be <110>. Therefore, an angle θ is formed between the first direction D1 and the second direction D2. In some embodiments, the angle θ is an acute angle. In some embodiments, the angle θ is in a range from about 40 degrees to about 50 degrees. For example, the angle θ is about 45 degrees. If the angle θ is out of the range (i.e., about 40 degrees to about 50 degrees), the height of the epitaxial layer 318 (also the semiconductor fins 318′ in FIG. 9) is increased to capture the defects, such that the size of the device is increased. The pitch between the strips is predetermined. The hard mask 320 contains a dielectric material that has a distinguishable etching rate from the epitaxial layer 318. The strips of the hard mask 320 span across the top surface of the epitaxial layer 318. The strips of the hard mask 320 have a width smaller than the width of each of the bar-like epitaxial layer 318, leaving portions of the epitaxial layer 318 exposed from the hard mask 320 as shown in FIG. 8.

Reference is made to FIG. 9. A portion of the epitaxial layer 318 is removed. After the patterning of the hard mask 320, the underlying epitaxial layer 318 is partially removed according to the pattern of the hard mask 320. In some embodiments, the exposed (i.e., not covered by the hard mask 320) portions of the epitaxial layer 318 is removed during an etching process, leaving voids 322 between the patterned epitaxial layers 318′. The epitaxial layer 318 has a distinguishable etching rate from the isolation region 314 and the hard mask 320. An etching selectivity is shown among the isolation region 314, the epitaxial layer 318, and the hard mask 320.

Reference is made to FIG. 10. The hard mask 320 of FIG. 9 is removed from the surface of the isolation region 314. The hard mask 320 may be removed by wet stripping and/or plasma ashing. The thin strip configuration of the hard mask 320 is translated to the underlying epitaxial layer 318, and the patterned, segmented patterned epitaxial layers 318′ are substantially aligned to each other along the <110> crystallographic direction. After the patterning, the trenches 316 re-emerge and divided by the patterned epitaxial layers 318′ into different compartments (i.e., voids 322). The interlaced pattern created between the trenches 316 and the patterned epitaxial layers 318′ arises from the different crystallographic directions. The trenches 316 remain in <100> crystallographic direction, while the patterned epitaxial layers 318′ are transformed from the <100> crystallographic direction to the <110> crystallographic direction. The offset arrangement creates discrete patterned epitaxial layers 318′ in one trench 316. Within one trench 316, voids 322 are interposed between the patterned epitaxial layers 318′.

Reference is made to FIG. 11. The voids 322 are then filled with a dielectric material. The dielectric material may overfill the surface of the isolation region 314, and a planarization process is performed to expose the patterned epitaxial layers 318′. In some embodiments, the dielectric material may be the same as the dielectric material used in the isolation region 314. In some embodiments, the dielectric material may be different from that of the isolation region 314. The trenches 316 in the <100> crystallographic direction cease to exist on the semiconductor substrate 310. The isolation region 314 retains and bears the patterned epitaxial layers 318′ in <110> crystallographic direction on the semiconductor substrate 310.

Reference is made to FIG. 12. An isolation region 314′ recessing process is performed. The patterned epitaxial layers 318′ protrude from the recessed surface of the isolation region 314′. An upper portion of the patterned epitaxial layers 318′ re-emerge as semiconductor fins. These patterned epitaxial layers 318′ are orientated toward the <110> crystallographic direction, while the formation process allows the lattice structure of the patterned epitaxial layers 318′ to be orientated toward the <100> crystallographic direction. The <100> crystallographic direction effectively confines <111> family threading dislocations when the epitaxial layer 318 is grown in the trenches 316. The epitaxial layer 318 is then transformed from the <100> crystallographic direction to the <110> crystallographic direction through the hard mask 320 patterning process. The patterned epitaxial layers 318′ (semiconductor fins) have a lattice structure that ensures <111> family defect confinement and suitable for semiconductor device processing.

In some embodiments, the patterned epitaxial layers 318′ are aligned along the <110> crystallographic direction in a column and offset to each other in respect to the row direction. As shown in FIG. 12, the patterned epitaxial layers 318′ in the first column are offset from the patterned epitaxial layers 318′ in the second column. This offsetting pattern arises from the arrangement of the hard masks 320.

The isolation region 314 recessing process also has a pivotal effect to maintain the patterned epitaxial layers 318′ (semiconductor fins) <111> family defect free. Reference is made to FIG. 14, illustrating a cross-sectional view along line I-I in FIG. 8. The epitaxial layer 318 is patterned into segmented strip orientated toward the <110> crystallographic direction. The depth of the trench 316 is similar to the height (thickness) of the patterned epitaxial layer 318′. As shown in FIG. 14, the height H of the patterned epitaxial layer 318′ is measured from the top surface of the semiconductor substrate 310 to the top surface of the patterned epitaxial layer 318′. The height H₁ is the minimum sidewall height that is capable to trap the <111> family threading dislocations. In some embodiments, the height H₁ of the patterned epitaxial layer 318′ is about 120 nm±10%. The semiconductor fin, which protrudes over the surface of the isolation region 314 and does not contain any <111> family threading dislocations 390 which may be 54 degree inclined to the plane of the substrate 310, has a height of about 70 nm. After subtraction (120 nm-70 nm), about 50 nm of height H₁ of the patterned epitaxial layer 318′ is enclosed by the sidewalls of the isolation region 314 so as to trap the threading dislocations. The minimum width W of the patterned epitaxial layer 318′ is measured along a direction substantially perpendicular to the <110> crystallographic direction, and the maximum width W satisfies the following equation: H ₁=tan(54°)×W

Alternatively, the maximum width W can be expressed as the follow:

$W = \frac{H_{1}}{{1.3}8}$

When the height H₁ is about 50 nm, it gives the maximum width W of the patterned epitaxial layer 318′ of about 36 nm.

Reference is made to FIG. 12 again. Each of the patterned epitaxial layers 318′ has a maximum length L measured along the <110> crystallographic direction. The length of one patterned epitaxial layer 318′ satisfies the following equation: L=W×√{square root over (2)}

The maximum length L is equal to the maximum width W times square root of 2. In some embodiments, when the width W is about 36 nm, the length L is about 51 nm (L=36×√{square root over (2)}). The length L of the patterned epitaxial layers 318′ is related to the width W, and the width W is determined by the height H₁. The dimension of the patterned epitaxial layers 318′ is guarded by the abovementioned equations.

FIG. 15 is a local top view of the semiconductor fins 318′ of FIG. 12. The semiconductor fin 318′ has a parallelogram top surface 318 t and a parallelogram bottom surface (i.e., the interface between the semiconductor fin 318′ and the semiconductor substrate 310. The parallelogram top surface 318 t has two acute interior angles a and two obtuse interior angles b. The acute interior angle a is in a range from about 40 degrees to about 50 degrees, and the obtuse interior angle b is in a range from about 130 degrees to about 140 degrees. For example, the acute angle a is about 45 degrees, and the obtuse interior angle b is about 135 degrees. Also, the parallelogram bottom surface have two acute interior angles a and two obtuse interior angles b. The shape of the parallelogram bottom surface is substantially the same as or similar to the shape the parallelogram top surface 318 t shown in FIG. 15. The semiconductor fin 318′ has source/drain regions 319 a and a channel region 319 b between the source/drain regions 319 a. The channel region 319 b is a region where a gate structure will be formed thereon, and the gate structure is not formed on the source/drain regions 319 a (e.g., the gate structure 452 and the semiconductor fin 422 of FIG. 16B). At least one of the source/drain regions 319 a has a tapered end E tapered away from the channel region 319 b. For example, the source/drain regions 319 a respectively have tapered ends E tapered away from the channel region 319 b. Also, the tapered end E of one of the source/drain regions 319 a is tapered away from another of the source/drain regions 319 a. The semiconductor fin 318′ has two opposite sidewalls 317 s and two opposite end walls 317 e. A sidewall 317 s and an end wall 317 e of the semiconductor fin 318′ form the tapered end E. Also, another sidewall 317 s and another end wall 317 e of the semiconductor fin 318′ form another tapered end E. The acute interior angle a is formed between the sidewall 317 s and the end wall 317 e of the semiconductor fin 318′.

The patterned epitaxial layers 318′ may be then fabricated into different semiconductor devices. Reference is made to FIGS. 16A through 16C, illustrating the transition from the patterned epitaxial layers to two inverters 40. FIG. 16A is a schematic diagram showing the relationship between the trenches 316 and the hard mask 320. The trenches 316 and the hard masks 320 are arranged in a fashion that allows the resulting patterned epitaxial layers 318′ to be in alignment in rows and in column. The arrangement of the trenches 316 arises from the configuration of the semiconductor pillars 312 as shown in FIG. 4. In some embodiments, an n-FET region and a p-FET region are arranged side by side as shown in FIG. 16A. Each of the hard masks 320 spans across two of the trenches 316, and therefore creating four semiconductor fins, two for each of the n-FET and p-FET regions. The two n-FETs and two p-FETs are made into two inverters 40.

Reference is made to FIG. 16B, illustrating a schematic diagram of the n-FETs and p-FETs. Two sets of semiconductor fins are yielded after the patterning process shown in FIG. 16A. The semiconductor fins (patterned epitaxial layers) are orientated to the <110> crystallographic direction suitable for subsequent fabrication process and aligned both in row and in column. The semiconductor fins 422 and 424 are originated from the hard mask 320 at the p-FET region, and the semiconductor fins 432 and 434 are originated from the hard mask 320 at the n-FET region. The semiconductor fins 422 and 424 are arranged along the <110> crystallographic direction, and the semiconductor fins 432 and 434 are arranged along the <110> crystallographic direction. The semiconductor fins 432 and 424 are arranged along the <100> crystallographic direction. That is, the semiconductor fins 432 and 424 are patterned from the same strip of the semiconductor pillar 312 (see FIG. 4). The semiconductor fins 422 and 432 are a pair of neighbouring p-FinFET and n-FinFET. The semiconductor fins 424 and 434 are also a pair of neighbouring p-FinFET and n-FinFET. A gate structure 452 is formed across the semiconductor fins 422 and 432. A gate structure 454 is formed across the semiconductor fins 424 and 434. The gate structures 452 and 454 may be formed by gate first or gate last process. In some embodiments, in the gate last process, a dummy gate is disposed over the semiconductor fins 422, 424, 432, and 434. After source and drain regions are formed, the dummy gate is removed, and a high-k dielectric layer, a barrier layer, a work function metal layer, and a metal gate electrode are then deposited to form a high-k metal gate.

Reference is made to FIG. 16C. Source and drain regions 462, 464, 472, and 474 are formed. The source and drain regions 462, 464, 472, and 474 are formed on either side of the semiconductor fins 422, 424, 432, and 434. Contact plugs 456 and 458 are formed over the gate structures 452 and 454 for electrical connection. The semiconductor fins (patterned epitaxial layers) 422, 424, 432, and 434 are then transformed into two adjacent inverters 40.

Due to rapid growth in use and applications of digital information technology, there are demands to continuingly increase the memory density of memory devices while maintaining, if not reducing, the size of the devices. Memory cells having increased capacity and smaller critical dimensions are greatly sought after. Stacks of memory cells may include phase change materials, switching diodes, charge storage structures (e.g., floating gate structures, charge traps, tunneling dielectrics), a stack of alternating control gate structures and dielectric materials, and charge blocking materials between the charge storage structures and adjacent control gate structures. The semiconductor fins fabricated according to the abovementioned process ensures <111> family threading dislocations free and a solid structure foundation.

Reference is made to FIGS. 17A through 17C, illustrating the transition from the patterned epitaxial layers to two NANDs 50. FIG. 17A is a schematic diagram showing the relationship between the trenches 316 and the hard masks 320 and 320′. In some embodiments, an n-FET and a p-FET regions are arranged side by side as shown in FIG. 17A. Each of the hard masks 320 and 320′ spans across two of the trenches 316, and therefore creating four semiconductor fins, two for each of the n-FET and p-FET regions. The two n-FETs and two p-FETs are made into two NANDs 50. The hard mask 320′ is different from the hard mask 320. The hard mask 320′ is broader in width than the hard mask 320. The resulting patterned epitaxial layer from the hard mask 320′ is measured wider than the neighbouring patterned epitaxial layer which uses had mask 320 as a template. The varied configuration of hard masks results in different patterned epitaxial layers. In some embodiments, the hard masks may have different width as shown in FIG. 17A. In some embodiments, the hard masks may have different length. In some embodiments, the width and length of the hard masks may both be different from each other. The hard masks may have variation in dimension and maintain the resulting patterned epitaxial layers toward the <110> crystallographic direction at the same time. It should be understood that hard mask variation in dimension does not interrupt the alignment among the patterned epitaxial layers. As shown in FIG. 17A, the resulting patterned epitaxial layers will be in alignment in row and in column regardless the width.

Reference is made to FIG. 17B, illustrating a schematic diagram of the n-FETs and p-FETs. Two sets of neighbouring semiconductor fins are yielded after the patterning process shown in FIG. 17A. The semiconductor fins (patterned epitaxial layers) are orientated to the <110> crystallographic direction suitable for subsequent fabrication process. The semiconductor fins 522 and 524 are originated from the hard mask 320′ at the p-FET region, and the semiconductor fins 532 and 534 are originated from the hard mask 320 at the n-FET region. The semiconductor fins 522 and 524 are arranged along the <110> crystallographic direction, and the semiconductor fins 532 and 534 are arranged along the <110> crystallographic direction. The semiconductor fins 532 and 524 are arranged along the <100> crystallographic direction. That is, the semiconductor fins 532 and 524 are patterned from the same strip of the semiconductor pillar 312 (see FIG. 4). Gate structures 652 a and 652 b are formed across the semiconductor fins 522 and 532. Gate structures 654 a and 654 b are formed across the semiconductor fins 524 and 534. Unlike the inverters shown in FIG. 14B, each pair of the n-FET and p-FET regions has two gate structures. The number of gate structures disposed on the semiconductor fins (patterned epitaxial layers) 522, 524, 532, and 534 is flexible depending on design choice. As shown in FIG. 17B, the semiconductor fins 522 and 532 accommodate two gate structures 652 a and 652 b making two pairs of neighbouring p-FinFETs and n-FinFETs. The semiconductor fins 524 and 534 accommodate two gate structures 654 a and 654 b making two pairs of neighbouring p-FinFETs and n-FinFETs. The gate structures 652 a, 652 b, 654 a, and 654 b may be formed by gate first or gate last process.

Reference is made to FIG. 17C. Source and drain regions 562, 564, 572, and 574 are formed. The source and drain regions 562, 564, 572, and 574 are formed on either side of the semiconductor fins 522, 524, 532, and 534. Contact plugs are designated as a cross with border in FIG. 17C. The contact plugs are electrically connected to the source and drain regions 562, 564, 572, and 574 and the gate structures 652 a, 652 b, 654 a, and 654 b. The semiconductor fins (patterned epitaxial layers) 522, 524, 532, and 534 are then transformed into two adjacent NANDs 50, and their n-FinFET and p-FinFET regions are of different dimensions.

When epitaxial layer is grown inside a <100> crystallographic direction predefined trenches with high aspect ratio on silicon substrate, all four of the <111> family threading dislocations will be trapped within the trench sidewalls, leaving the top portion defect-free. This aspect-ratio-trapping (ART) technique utilizes geometrical defect annihilation technique. The semiconductor fins are then transformed from <100> crystallographic direction to the industrial standard <110> crystallographic direction by photolithography and patterning process. The transformation allows the semiconductor fins to remain defect free and to be easily handled.

According to some embodiments, a semiconductor device includes a plurality of semiconductor fins and a gate structure. The semiconductor fins have parallelogram top surfaces, the parallelogram top surface has two acute interior angles and two obtuse interior angles, two of the semiconductor fins are arranged along <110> crystallographic direction, and two of the semiconductor fins are arranged along <100> crystallographic direction. The gate structure is over at least one of the semiconductor fins.

According to some embodiments, a semiconductor device includes first and second semiconductor fins arranged along a first direction; third and fourth semiconductor fins arranged along the first direction, wherein third and fourth semiconductor fins have a type dopant different from that of the first and second semiconductor fins; a first gate structure extending across the first and third semiconductor fins along a second direction; and a second gate structure extending across the second and fourth semiconductor fins along the second direction, wherein the first and fourth semiconductor fins are arranged along a third direction crossing the first and second directions, and the third direction is parallel with a <100> crystallographic direction.

According to some embodiments, a semiconductor device includes a first semiconductor fin, wherein the first semiconductor fin has a top surface that has a first edge extending along <110> crystallographic direction, a second edge substantially parallel with the first edge, and a third edge obliquely connected between the first edge and the second edge and extending along <100> crystallographic direction; and a first gate structure over the first semiconductor fin.

The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure. 

What is claimed is:
 1. A semiconductor device, comprising: a plurality of semiconductor fins, wherein the semiconductor fins have parallelogram top surfaces, the parallelogram top surface has two acute interior angles and two obtuse interior angles, a first one and a second one of the semiconductor fins are aligned along <110> crystallographic direction, and the second one and a third one of the semiconductor fins are aligned along <100> crystallographic direction; and a gate structure over at least one of the semiconductor fins.
 2. The semiconductor device of claim 1, wherein the first one and the second one of the semiconductor fins aligned along <110> crystallographic direction have the same type dopants, and the the second one and the third one of the semiconductor fins aligned along <100> crystallographic direction have different type dopants.
 3. The semiconductor device of claim 1, wherein the first one and the second one of the semiconductor fins aligned along <110> crystallographic direction have the same width, and the the second one and the third one of the semiconductor fins aligned along <100> crystallographic direction have different widths.
 4. The semiconductor device of claim 1, wherein a distance between the first one and the second one of the semiconductor fins aligned along <110> crystallographic direction is less than a distance between the the second one and the third one of the semiconductor fins aligned along <100> crystallographic direction.
 5. The semiconductor device of claim 1, further comprising a semiconductor substrate under the semiconductor fins, wherein an interface of one of the first to third ones of the semiconductor fins and the semiconductor substrate is parallelogram, and the interface has two acute internal angles and two obtuse internal angles.
 6. The semiconductor device of claim 5, wherein the semiconductor substrate and said one of the first to third ones of the semiconductor fins have different materials.
 7. The semiconductor device of claim 1, wherein at least one of the first to third ones of the semiconductor fins has a source region, a drain region and a channel region between the source region and the drain region, the gate structure is over the channel region, and the source region has a tapered end farthest from the channel region from a top view.
 8. The semiconductor device of claim 7, wherein the drain region has a tapered end farthest from the channel region and misaligned with the tapered end of the source region from the top view.
 9. A semiconductor device, comprising: a first semiconductor fin, wherein the first semiconductor fin has a top surface that has a first edge extending along <110> crystallographic direction, a second edge substantially parallel with the first edge, and a third edge obliquely connected between the first edge and the second edge and extending along <100> crystallographic direction; and a first gate structure over the first semiconductor fin.
 10. The semiconductor device of claim 9, further comprising: a second semiconductor fin, wherein the second semiconductor fin has a top surface having a fourth edge extending along <110> crystallographic direction, a fifth edge substantially parallel with the fourth edge, and a sixth edge obliquely connected between the fourth edge and the fifth edge and extending along <100> crystallographic direction, wherein the first gate structure is further over the second semiconductor fin.
 11. The semiconductor device of claim 9, further comprising: a second semiconductor fin, wherein the second semiconductor fin has a top surface having an edge extending along <100> crystallographic direction and substantially aligned with the third edge of the top surface of the first semiconductor fin along <100> crystallographic direction; and a second gate structure over the second semiconductor fin.
 12. The semiconductor device of claim 9, further comprising an isolation region laterally surrounding the first semiconductor fin, wherein a width of the first semiconductor fin is less than a height of a portion of the first semiconductor fin enclosed by the isolation region divided by tan (54°).
 13. A device, comprising: a substrate having a <110> crystallographic direction and a <100> crystallographic direction; a first fin extending over the substrate and along a first direction substantially parallel with the <110> crystallographic direction; a second fin extending over the substrate and along the first direction, wherein the first fin is substantially aligned with the second fin in the first direction; a third fin extending over the substrate and along a second direction substantially parallel with the <110> crystallographic direction, wherein the first fin is substantially aligned with the third fin in a third direction substantially parallel with the <100> crystallographic direction; a first gate structure over a channel region of the first fin; and a second gate structure over a channel region of the second fin and over a channel region of the third fin.
 14. The device of claim 13, further comprising: an isolation region surrounding the first to third fins, wherein the isolation region has a first sidewall facing the first fin, and the first sidewall of the isolation region extends along a fourth direction substantially parallel with the <100> crystallographic direction.
 15. The device of claim 14, wherein the isolation region has a second sidewall facing the first fin and adjacent the first sidewall of the isolation region, and the second sidewall of the isolation region extends along a fifth direction substantially parallel with the <111> crystallographic direction.
 16. The device of claim 15, wherein the isolation region has a third sidewall facing the first fin, the second sidewall of the isolation region is connected between the first and third sidewall of the isolation region, and the third sidewall of the isolation region extends along a sixth direction substantially parallel with the <100> crystallographic direction.
 17. The device of claim 14, wherein the isolation region has a fourth sidewall facing the second fin, and the fourth sidewall of the isolation region extends along a seventh direction substantially parallel with the <100> crystallographic direction.
 18. The device of claim 14, wherein the first sidewall of the isolation region has a first end and a second end, and the channel region of the first fin is closer to the first end of the first sidewall of the isolation region than the second end of the first sidewall of the isolation region.
 19. The device of claim 13, wherein a distance between the second fin and the third fin is greater than a distance between the first fin and the second fin.
 20. The device of claim 13, wherein the first and second gate structures extend along a fourth direction substantially perpendicular to the <110> crystallographic direction. 